The formation and types of hot melt adhesive film

PO hot melt adhesive film	PA hot melt adhesive film

Hot melt adhesive film, also known as hot melt glue film, which is similar to double sided fusible interfacing. This product consists a layer of film and release paper. The adhesive film feels like ordinary film without stickiness in normal temperature, after heated to the melting point, the film layer has strong viscosity, can bond two kinds of materials permanently.

Hot melt adhesive film has many advantages, such as environmental protection, wide range of sticky, bonding rapidly and so on. Generally produced by EAA, PA, PES, TPU, EVA, single or multiple synthesis of material production, mainly used for textile fabric, leather, plastic, foam, electronic field, metal composite.

EVA hot melt film
Base material: single silicon mold of paper
Thickness: 0.04-0.25 mm
Ironing temperature: 110-130 ℃
Press time: 6-10 s
Usage: PET, leather, non-woven fabric, wood, paper, and other areas of the joint.

PA hot melt film
Thickness: 0.05-0.25 mm
Ironing temperature: 150-180 ℃
Press time: 12-20 s
Scope of application: embroidered badges, trademark back glue, etc

PES film
Thickness: 0.05-0.25 mm
Ironing temperature: 140-160 ℃
Press time: 12 to 18 s
Application: conductive fabric, embroidered badges, woven label back glue, flocking printing, textiles, PVC high frequency joint, etc.

PO hot melt film
Thickness: 0.04-0.25 mm
Ironing temperature: 130-160 ℃
Adhesive scope: bonding of aluminum and other metals.

TPU hot melt film
Thickness: 0.05-0.25 mm
Ironing temperature: 120-150 ℃
Press time: 10-20 s
The curing speed: 4 min
Adhesive range: nylon, lycra, polyester, blended fabrics, wool, cotton, leather, ABS, TPU, paper and various elastic fabric composite processing.